In recent years, metal single-atom catalysts (M-SACs) have attracted growing attention for PEM water electrolysis. Because each metal atom acts as an active catalytic site, these materials use precious metals far more efficiently than conventional catalysts, potentially lowering costs while improving performance. However, in high-density M-SACs, which are most favourable for PEMWEs, metal atoms tend to aggregate either during synthesis or electrolysis, reducing both catalytic activity and durability.
To address this issue, a research team led by Assistant Professor Jitendra N. Tiwari and Professor Young-Kyu Han from the Department of Energy and Materials Engineering at Dongguk University in South Korea have developed an innovative synthesis method for M-SACs. "Our technique utilises metal hydroxides as sacrificial templates, co-reducing them in a two-step high-temperature heat-treatment process," explained Dr Tiwari. "This process effectively prevents the aggregation of metal atoms due to steric hindrance, creating atomically dispersed metal single-atom catalysts." Their study was made available online on 28 October 2025 and published in Volume 168 of Materials Science & Engineering R in January 2026.
Using β-nickel hydroxide (β-Ni(OH)2) as the template, the researchers synthesized platinum (Pt)-based single atom catalysts called β-PtSAsS800 and β-PtSAsS850. In the process, a dried mixture of β–Ni(OH)2, Pt precursors, and dicyandiamide, was subjected to pyrolysis at 850°C or 800°C under a nitrogen atmosphere. The β–Ni(OH)2 template limits the mobility of metal ions in the mixture, while dicyandiamide provides carbon (C) and nitrogen(N). The final structure of the catalysts consists of single Pt atoms bonded to N atoms, atomically dispersed on graphitic nanosheets.
The synthesised catalysts demonstrated outstanding catalytic performance, with β-PtSAsS850 achieving an extraordinarily low overpotential of 15 millivolts and turnover frequencies 72 - 78-fold higher than commercial Pt/C catalysts. The material also demonstrated impressive durability, maintaining its structure and performance for more than 10 days of continuous testing. Notably, the β-PtSAsS850-based PEMWE system surpassed the US Department of Energy 2026 target, indicating its potential for industrial applications. It also demonstrated robust performance for over 200 hours.
Theoretical calculations and experiments showed that this enhanced performance is due to the PtN2 catalytic sites within graphitic sheets, which significantly lower the energy barrier for hydrogen production. The researchers also synthesised M-SACs with other metals like iridium, palladium and ruthenium, demonstrating the generalisability of the approach.
"Our strategy offers a new way for synthesising highly active M-SACs, valuable for developing highly efficient energy conversion and storage devices," concluded Young-Kyu Han. "Moreover, the excellent performance of the synthesised catalysts in electrolysis could help make hydrogen more economically competitive with fossil fuels for the first time. In the long term, this will accelerate hydrogen adoption, contributing to the fight against climate change."